Method for adjusting the threshold voltage of a gate stack of a pmos device

ABSTRACT

A method for fabricating a semiconductor device comprising a gate stack of a gate dielectric and a gate electrode, the method including forming a gate dielectric layer over a semiconductor substrate the gate dielectric layer being a metal oxide or semimetal oxide having a first electronegativity; forming a dielectric V T  adjustment layer, the dielectric V T  adjustment layer being a metal oxide or semimetal oxide having a second electronegativity; and forming a gate electrode over the gate dielectric layer and the V T  adjustment layer; wherein the Effective Work Function of said gate stack is tuned to a desired value by tuning the thickness and composition of the dielectric V T  adjustment layer and wherein the second electronegativity value is higher than both the first electronegativity value and the electronegativity of Al 2 O 3

FIELD OF THE INVENTION

This invention relates to the field of gate stacks for semiconductor devices, in particular gate stacks having an adjustable threshold voltage.

BACKGROUND

A major challenge to make high-k metal oxides as gate dielectric successful in gate stacks for transistors is finding appropriate electrodes with stable band-edge Effective Work Functions (EWF) in order to meet the threshold voltage (V_(T)) specifications for a gate stack in silicon technology as defined by the International Roadmap for Semiconductors (ITRS). For NMOS transistors the EWF of the gate stack needs to be high (closer to the Si conduction band edge) and for PMOS stacks, the EWF needs to be low (closer to the Si valence band edge). For NMOS devices a gate dielectric is deposited over a p-type gate region of a semiconductor substrate. In the on-state of the NMOS transistor, an n-type conductive channel is formed in the p-type gate area, between the n-type source and drain regions. For PMOS devices a gate dielectric is formed over an n-type gate region. One of the techniques known in the art for adjusting the EWF of the gate stack is adjusting the composition of the metal electrode; see e.g. US Patent Application Publication 2004/0106261 and U.S. Pat. No. 6,846,734. The value of the EWF of a gate stack is influenced by the electronegativity of the different elements and compounds composing the gate stack. Adding elements or compounds, which are more electronegative/electropositive than the host high-k dielectric tends to shift the EWF in positive/negative direction respectively. More recently, capping of the gate dielectric by using ultra-thin dielectric cap layer has been used to tune the EWF of the gate stack towards the desired values, e.g. IEEE Electron. Dev. Lett. 28(6), 486-488 (2007); IEEE Transactions on Electron. Dev. 54(10) 2738-2749 (2007); ECS Transactions 11(7) 201-211 (2007); ECS Transactions 19(1) 253-261, (2009). Typically, La based dielectric caps are used for NMOS and Al based caps for PMOS. The VFB shift with Al₂O₃ capping layers is only about 200 mV and not meeting requirements for 32 nm High Performance (HP) PMOS logic transistors. When increasing the thickness of the Al₂O₃ film, the V_(T) shift only hardly increases and, because of the low k value of the Al₂O₃ layer, the EOT penalty significantly increases, which is unacceptable. Alternative cap layers are desirable, in particular for PMOS devices.

SUMMARY OF THE INVENTION

It is an object of the invention to provide an improved method for manufacturing an integrated circuit comprising a gate stack of a gate dielectric and a gate electrode over a semiconductor substrate in which method the V_(T) value of the gate stack can easily be adjusted.

According to an embodiment, a method is provided for fabricating a semiconductor device comprising a gate stack of a gate dielectric and a gate electrode, the method comprising the steps of: forming a gate dielectric layer over a semiconductor substrate the gate dielectric layer being a metal oxide or semimetal oxide having a first electronegativity value; forming a dielectric V_(T) adjustment layer, the dielectric V_(T) adjustment layer being a metal oxide or semimetal oxide having a second electronegativity; and forming a gate electrode over the gate dielectric layer and the V_(T) adjustment layer; wherein the Effective Work Function of said gate stack is tuned to a desired value by tuning the thickness and composition of the dielectric V_(T) adjustment layer and wherein the second electronegativity value is higher than both the first electronegativity value and the electronegativity of Al₂O₃. In a preferred embodiment the metal or semimetal of the V_(T) adjustment layer is selected from one of the following five groups: Group 1: Ti; Group 2: Mo, W; Group 3: Pb; Group 4: Sb, Bi; Group 5: Ge. The V_(T) adjustment layer can be provided under, over or midway the high-k gate dielectric layer.

According to another embodiment of the present invention, a method is provided for fabricating a semiconductor device comprising a gate stack of a gate dielectric and a gate electrode, the method comprising the steps of: forming a gate dielectric layer over a semiconductor substrate, the gate dielectric layer being a metal oxide or semimetal oxide wherein the metal or semimetal having a first electronegativity; doping the gate dielectric layer with a one or more dopant elements having a second electronegativity; and forming a gate electrode over the gate dielectric layer and the V_(T) adjustment layer; wherein the Effective Work Function of said gate stack is tuned to a desired value by selecting the type and amount of dopant elements layer and wherein the second electronegativity is higher than the first electronegativity.

According to yet another embodiment of the present invention, a method is provided for fabricating a semiconductor device comprising a gate stack of a gate dielectric and a gate electrode, the method comprising the steps of: forming a gate dielectric layer over a semiconductor substrate; forming a dielectric V_(T) adjustment layer containing Ge, Sb or Te in any composition thereof over the gate dielectric layer; and forming a gate electrode over the gate dielectric layer and the V_(T) adjustment layer; wherein the Effective Work Function of said gate stack is tuned to a desired value by tuning the thickness and composition of said V_(T) adjustment layer.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 shows a periodic table of electronegativity values of the elements.

FIG. 2 shows electronegativity values of some elements and their oxides.

FIG. 3 shows possible positions in the gate stack of dielectric V_(T) adjustment layers.

FIG. 4 shows CV curves for gate stacks having a Bi₂O₃ V_(T) adjustment layer.

FIG. 5 shows CV curves for gate stacks having a TiO2 V_(T) adjustment layer.

DETAILED DESCRIPTION OF THE INVENTION

As a dielectric V_(T) adjustment layer, metal oxides wherein the metal is selected from one of the following five groups can be used based on the electronegativity of the metals: Group 1: Ti; Group 2: Mo, W; Group 3: Pb; Group 4: Sb, Bi; Group 5: Ge; FIG. 1 shows a periodic table of the elements giving the electronegativity of the respective elements. For a compound A_(x)B_(y) the electronegativity of the compound EN(A_(x)B_(y)) can be calculated based on the electronegativity of the composing elements EN(A) and EN(B) according to the Sanderson Criterion: EN(A_(x)B_(y))=(EN(A)^(x)·EN(B^()y))^(1/(x+y)). The values for a selected number of elements and their oxides are shown in FIG. 2, see also ECS Transactions 19(1) 253-261, (2009). The position of the V_(T) adjustment layer can be selected below, midway or above the high-k gate dielectric layer as shown in FIG. 3.

Instead of using a dielectric V_(T) adjustment layer of a metal oxide, also doping of the high-k gate dielectric can be used. Preferably the top of the gate dielectric layer is doped with one or more elements having a high electronegative value. Alternatively the interface between the Si substrate and the gate dielectric layer can be doped with one or more elements having a high electronegative value. In particular Fluorine is suitable for this purpose as it has an extremely high electronegative value and in general fluorine is compatible with semiconductor processing. Suitable precursors for fluorine doping are F2, NF3, TiF4 and TaF5. Other halides can also be used.

Finally, adding a layer containing Ge, Sb or Te (GST) in any composition thereof to the gate electrode metal is contemplated. Such a layer is beneficial because all three of its components have high electronegativity and are suitable for ALD deposition. The GST adjustment layer is preferably deposited directly on top of the gate dielectric layer.

Example 1

On p-type silicon substrates first a ˜1 nm SiO₂ interfacial layer was grown and then a 2 nm HfO₂ high-k gate dielectric layer was deposited with an ALD process using HfCl₄ and H₂O chemistry. A 1 nm Bi₂O₃ V_(T) adjustment layer was deposited over the HfO₂ gate dielectric using an ALD process and Bi(dmb)₃+H₂O chemistry as described in US Patent Publication No. 2007-148347 by Hatanpää et al. which is incorporated herein by reference. Anneals at 800 and 900° C. in N2 for 10 minutes were performed. A top electrode of Pt was deposited by Physical Vapor Deposition. C-V curves for a HfO₂ reference sample, and for samples with the 1 nm Bi₂O₃ V_(T) adjustment layer on top of the HfO₂ layer are shown in FIG. 4. As we used capacitors in this simplified experiment, we consider relative flatband voltage (V_(FB)) shift compared to the HfO₂ reference instead of V_(T) shift. For the as-grown Bi₂O₃ V_(T) adjustment layer, the shift in V_(FB) is 0.7 V in the positive direction and for the 800 and 900° C. annealed samples the shift in V_(FB) is still 0.5 V or larger. If such V_(FB) shifts would occur in a transistor processed in a regular device flow with a metal electrode like TiN, it would bring the EWF to the Si valence band edge and hence V_(T) to the low target value required for HP PMOS transistors. The V_(T) adjustment layers are not deteriorating the CV curves, indicating that there is no negative impact on the SiO₂/HfO₂ interface quality. No severe EOT degradation was observed due to the addition of Bi₂O₃ V_(T) adjustment layers.

Example 2

On p-type silicon substrates first a ˜1 nm SiO₂ interfacial layer was grown and then a 2 nm HfO₂ high-k gate dielectric layer was deposited with an ALD process using HfCl₄ and H₂O chemistry. A 0.5 nm TiO₂ V_(T) adjustment layer was deposited using an ALD process with Ti(OCH₄)₃+H₂O chemistry. Alternative chemistries for the TiO₂ deposition can be used like TiCl₄, Ti(OC₃H₇)₄ and (Me₅Cp)Ti(OMe)₃. An anneal at 800° C. in N₂ for 10 minutes was performed. A top electrode of Pt was deposited by Physical Vapor Deposition. C-V curves for a HfO₂ reference sample, and for the samples with the 0.5 nm TiO₂ V_(T) adjustment layer over the HfO₂ are shown in FIG. 5. The TiO₂ layer showed a V_(FB) shift of about 0.35 V.

Example 3

For doping of the gate dielectric layer the following proposed processing sequence could be used: grow a ˜1 nm SiO₂ interfacial layer on a silicon substrate and then deposit a 2 nm HfO₂ high-k gate dielectric layer with an ALD process using HfCl₄ and H₂O chemistry; expose the HfO₂ gate dielectric to a fluorine containing gas; then deposit a top electrode. The conditions of the exposure to the fluorine containing gas are selected such that the EWF obtains a desired value.

Example 4

We propose the following experiment. A ˜1 nm SiO₂ interfacial layer can be grown silicon substrates and then a 2 nm HfO₂ high-k gate dielectric layer can be deposited with an ALD process using HfCl₄ and H₂O chemistry. Then a 1-10 nm thick V_(T) adjustment layer containing Ge, Sb or Te in any composition thereof can be deposited over the high-k dielectric layer. The GeSbTe layer can be deposited with an ALD process using GeCl₂.C₄H₈O₂, SbCl₃ and (Et₃Si)₂Te as precursors for respectively Ge, Sb or Te. The top electrode will be Pt, TaN, TiN or Al.

The experiments described in example 1 and 2 may not be fully representative of the situation in a full CMOS transistor device. In a transistor device a different metal electrode choice likely will be used and the gate stack might be subjected to different (higher or lower) temperatures and treatments than in these examples. The resulting EWF value of an actual gate stack after the process flow is determined by several convoluting effects: metal deposition technique, metal thickness, anneal conditions, intermixing of V_(T) adjustment layer with host high-k dielectric, intermixing of host high-k dielectric with SiO₂ interfacial layer, diffusion of V_(T) adjustment layer towards SiO₂ interfacial layer, etc. This means that obtaining the same (or even larger) shift of V_(FB) or EWF as demonstrated in example 1 and 2, may depend on an optimal choice of metal electrode or other process steps used.

Although in the present disclosure the chemical formula's are used for Hafnium Oxide (HfO₂), Bismuth Oxide (Bi₂O₃) and Titanium Oxide (TiO₂), the actual oxides may deviate from the stoichiometric composition and are understood to be included in the present description. 

1. A method for fabricating a semiconductor device comprising a gate stack of a gate dielectric and a gate electrode, the method comprising the steps of: forming a gate dielectric layer over a semiconductor substrate the gate dielectric layer being a metal oxide or semimetal oxide having a first electronegativity; forming a dielectric V_(T) adjustment layer, the dielectric V_(T) adjustment layer being a metal oxide or semimetal oxide having a second electronegativity; and forming a gate electrode over the gate dielectric layer and the V_(T) adjustment layer; wherein the Effective Work Function of said gate stack is tuned to a desired value by tuning the thickness and composition of the dielectric V_(T) adjustment layer and wherein the second electronegativity value is higher than both the first electronegativity value and the electronegativity of Al₂O₃.
 2. The method of claim 1 wherein the metal having the second electronegativity is selected from one of the following groups: Group 1: Ti; Group 2: Mo and W; Group 3: Pb; Group 4: Sb and Bi; Group 5: Ge.
 3. The method of claim 2 wherein the metal having the second electronegativity is selected from Group 1: Ti.
 4. The method of claim 2 wherein the metal having the second electronegativity is selected from Group 2: Mo and W.
 5. The method of claim 2 wherein the metal having the second electronegativity is selected from Group 3: Pb.
 6. The method of claim 2 wherein the metal having the second electronegativity is selected from Group 4: Sb and Bi.
 7. The method of claim 1 wherein the metal having the second electronegativity is selected from Group 5: Ge.
 8. The method of claim 1 wherein the metal oxide is Bi₂O₃
 9. The method of claim 1 wherein the V_(T) adjustment layer is formed over the semiconductor substrate and under the gate dielectric layer.
 10. The method of claim 1 wherein the V_(T) adjustment layer is formed over the gate dielectric layer.
 11. The method of claim 1 wherein the V_(T) adjustment layer is positioned midway the gate dielectric layer.
 12. A method for fabricating a semiconductor device comprising a gate stack of a gate dielectric and a gate electrode, the method comprising the steps of: forming the gate dielectric layer over a semiconductor substrate, the gate dielectric being a metal oxide or semimetal oxide wherein the metal or semimetal having a first electronegativity; doping the gate dielectric layer with one or more elements having a second electronegativity; forming the gate electrode over the doped gate dielectric layer; wherein doping the gate dielectric layer comprises tuning the Effective Work Function of said gate stack to a desired value by tuning the amount and type of dopant and wherein the second electronegativity is higher than the first electronegativity.
 13. The method of claim 12 wherein the dopant is a halide.
 14. The method of claim 13 wherein the dopant is fluorine.
 15. The method of claim 14 wherein doping comprises exposing the gate dielectric layer to F2, NF3, TiF4 or TaF5.
 16. A method for fabricating a semiconductor device comprising a gate stack of a gate dielectric layer and a gate electrode, the method comprising the steps of: forming the gate dielectric layer over over PMOS regions of a semiconductor substrate; forming a V_(T) adjustment layer containing Ge, Sb or Te in any composition thereof over the gate dielectric layer; and forming a gate electrode over the gate dielectric layer and the V_(T) adjustment layer; wherein the Effective Work Function of said gate stack is tuned to a desired value by tuning the thickness and composition of the dielectric V_(T) adjustment layer. 